• Login
    View Item 
    •   UMB Digital Archive
    • School, Graduate
    • Theses and Dissertations All Schools
    • View Item
    •   UMB Digital Archive
    • School, Graduate
    • Theses and Dissertations All Schools
    • View Item
    JavaScript is disabled for your browser. Some features of this site may not work without it.

    Browse

    All of UMB Digital ArchiveCommunitiesPublication DateAuthorsTitlesSubjectsThis CollectionPublication DateAuthorsTitlesSubjects

    My Account

    LoginRegister

    Statistics

    Display statistics

    Novel Bioactive Low-shrinkage-stress Nanocomposite with Antibacterial and Remineralization Properties and Thermal-cycling and Aging Resistance.

    • CSV
    • RefMan
    • EndNote
    • BibTex
    • RefWorks
    Thumbnail
    Name:
    Filemban_umaryland_0373D_11397.pdf
    Size:
    1.943Mb
    Format:
    PDF
    Download
    Author
    FILEMBAN, HANAN cc
    Advisor
    Xu, Huakun H.
    Weir, Michael D.
    Date
    2022
    Type
    dissertation
    
    Metadata
    Show full item record
    Abstract
    Dental composites continue to be the material of choice in daily dental practice for several reasons, including their good mechanical properties, conservative cavity design, and superior esthetics. However, the longevity of current resin composite restorations ranges only 5-10 years. Recurrent caries and tooth fracture are the most common types of failure during the first 6 years of clinical service. These failures are often caused by the polymerization shrinkage stress of the dental composite materials. Thus, there is an increased need to develop a new generation of bioactive dental composite with the ability to reduce polymerization shrinkage stress, long-term antibacterial, remineralization abilities, and excellent mechanical properties. Therefore, this dissertation aims to develop a new bioactive low-shrinkage-stress dental composite containing dimethylaminohexadecyl methacrylate (DMAHDM) and nanoparticles of amorphous calcium phosphate (NACP) which could be a promising approach to increase the chances of success of composite restorations and strengthen tooth structures. First, we found that the new bioactive low-shrinkage-stress resin composite significantly reduced the polymerization shrinkage stress, without compromising their mechanical properties. Increasing the DMAHDM mass fraction increased the antibacterial effect in a dose-dependent manner. Next, we investigated the low-shrinkage-stress composite mechanical stability and antibacterial durability in thermal cycling for 20,000 cycles, equivalent to two years of clinical life. We found that the bioactive low-shrinkage-stress composite possessed good mechanical properties that matched commercial composite both before and after thermal cycling. The new composite had potent antibacterial activity, which was maintained and did not decrease after thermal cycling. Lastly, we further examined the mechanical and antibacterial durability of a bioactive low-shrinkage-stress after 50,000 and 100,000 thermal cycles which corresponds to 5 and 10 years respectively of in vivo function. We found that the bioactive low-shrinkage-stress composite maintained its antibacterial potency after thermal cycling, indicating long-term antibacterial durability. In addition, it possessed good mechanical properties that were comparable to commercial composite both before and after thermal cycling. The triple benefits of antibacterial, remineralization, and lower shrinkage stress have a great potential to inhibit recurrent caries and increase restoration longevity.
    Description
    University of Maryland, Baltimore. Biomedical Sciences-Dental School. Ph.D. 2022.
    Keyword
    Nanocomposites
    Anti-Bacterial Agents
    Polymerization
    Methacrylates
    Identifier to cite or link to this item
    http://hdl.handle.net/10713/20361
    Collections
    Theses and Dissertations School of Dentistry
    Theses and Dissertations All Schools

    entitlement

     
    DSpace software (copyright © 2002 - 2023)  DuraSpace
    Quick Guide | Policies | Contact Us | UMB Health Sciences & Human Services Library
    Open Repository is a service operated by 
    Atmire NV
     

    Export search results

    The export option will allow you to export the current search results of the entered query to a file. Different formats are available for download. To export the items, click on the button corresponding with the preferred download format.

    By default, clicking on the export buttons will result in a download of the allowed maximum amount of items.

    To select a subset of the search results, click "Selective Export" button and make a selection of the items you want to export. The amount of items that can be exported at once is similarly restricted as the full export.

    After making a selection, click one of the export format buttons. The amount of items that will be exported is indicated in the bubble next to export format.